How does the hookah charcoal tablet press machine turn coconut shell into a high-end product?

In the field of special charcoal product manufacturing, the production process of the hookah charcoal tablet press machine directly affects the product quality. Natural coconut shells can be converted into high-quality hookah charcoal through three key steps: crushing, carbonization, and tableting.

In the raw material pretreatment stage, the coconut shell is crushed into 10-20mm particles by a hammer crusher, and after classification by a vibrating screen, it is sent to the carbonization furnace. The carbonization process is carried out at a high temperature of 850℃ for 120 minutes to ensure that the coconut shell is completely carbonized. The carbonized coconut shell charcoal is processed by an air flow mill, and the particle size is controlled at 200-300 mesh to prepare for subsequent tableting.

In the forming stage of the hookah charcoal tablet press, the coconut shell charcoal powder is mixed with 5% natural binder and stirred at a constant temperature of 80℃ for 30 minutes. The precision hookah charcoal tablet press is used to form at a pressure of 60MPa. The mold temperature is maintained at 90℃ to ensure uniform density of the charcoal sheet. The thickness of the formed carbon sheet is controlled at 4mm, the diameter is 33mm, and it has a regular geometric shape and a uniform honeycomb structure.

The finished hookah charcoal has excellent performance indicators: the burning time is up to 120 minutes, the ash content is less than 3%, and the calorific value is more than 7500kcal/kg. After testing, all indicators of the product meet the international hookah charcoal standards, providing consumers with a pure and lasting use experience. This standardized production process is driving the hookah charcoal industry to develop in a higher quality direction.